Description
The standard mix ratio is 2.5:1 Base to Liquid.
The finished colour is basically white, but with a peachy/pink tone. If you want a pure white cast, you need to add the Jesmonite White Pigment. Pigment should be added at a maximum of 2%.
SEE USER GUIDE
AC100 Specifications
- Mix Ratio 2.5:1 Base to Liquid by weight
- Wet Density 1845 kg/m3
- Dry Density 1745 kg/m3
- Initial set 15 – 20 minutes (18°C, No Retarder)
- Demould 2 hours (fully set 24 hours)
- Expansion on set 0.15%
Other Properties
- Compressive Strength 25 – 30 MPa
- Tensile Strength (UTS) 25 – 35 Mpa
- Bending Elastic Limit (LOP) 15 – 20 Mpa
- Bending Strength (MOR) 50 – 65 Mpa
- Youngs Modulus 5 – 6 Mpa
- Impact Strength (Charpy) 30 KJ/m²
- Moisture Movement <1%
- Fire resistance B.S.476 Part 6&7 – Class ‘O’
- Freeze/Thaw resistance Excellent -Test specimens undamaged
- Wet/Dry 50 Cycles Test specimens undamaged
Application Areas
Cast and laminated decorative mouldings, and with the inclusion of suitable glass reinforcements can be utilised for lightweight, high-impact panels. Jesmonite provides a fire-resistant coating for many expanded foams for theme park and theatre props.
Key Attributes
- Solvent-free – No VOC’s
- Good abrasion resistance and impact strength
- High Compressive and tensile strength
- Rapid curing and high early strength gain
Jesmonite Base
Jesmonite Base is the powder part used with AC100 Liquid and AC300 Liquid. Formerly known as Jesmonite AC Powder.
- Mix ratio: 2.5 Base: 1 Liquid by weight.
It is also possible to mix the material at a 3:1 ratio to produce a fast set which can be used to fill joints, air bubbles, or joint castings.